We are using cookies to implement functions like login, shopping cart or language selection for this website. Furthermore we use Google Analytics to create anonymized statistical reports of the usage which creates Cookies too. You will find more information in our privacy policy.
OK, I agree I do not want Google Analytics-Cookies
The Journal of Adhesive Dentistry



Forgotten password?


Dear readers,

our online journals are moving. The new (and old) issues of all journals can be found at
In most cases you can log in there directly with your e-mail address and your current password. Otherwise we ask you to register again. Thank you very much.

Your Quintessence Publishing House
J Adhes Dent 22 (2020), No. 4     24. July 2020
J Adhes Dent 22 (2020), No. 4  (24.07.2020)

Page 399-407, doi:10.3290/j.jad.a44871, PubMed:32666066

Chemical, Mechanical and Biological Properties of an Adhesive Resin with Alkyl Trimethyl Ammonium Bromide-loaded Halloysite Nanotubes
Garcia, Isadora Martini / Leitune, Vicente Castelo Branco / Arthur, Rodrigo Alex / Nunes, Julia / Visioli, Fernanda / Giovarruscio, Massimo / Sauro, Salvatore / Collares, Fabrício Mezzomo
Purpose: The aim of this study was to evaluate the chemomechanical properties, antibacterial activity, and cytotoxicity of an experimental adhesive resin containing halloysite nanotubes (HNT), doped with alkyl trimethyl ammonium bromide (ATAB).

Materials and Methods: A filler of HNT doped with ATAB was obtained (ATAB:HNT) and incorporated (5 wt%) into a resin blend made of bisphenol A glycerolate dimethacrylate, 2-hydroxyethyl methacrylate and a photoinitiator/co-initiator system (GATAB:HNT). The same resin blend without ATAB:HNT was used as control (Ctrl). The ATAB:HNT filler was assessed by scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The two tested adhesives were evaluated for degree of conversion (DC) in vitro and in situ, softening in alcohol, dentin microtensile bond strength (µTBS), antibacterial activity, and cytotoxicity (n = 5).

Results: SEM showed that the nanotubes had a characteristic tubular-needle morphology, while the TEM analysis confirmed the presence of ATAB inside the lumens of HNT. The incorporation of ATAB:HNT induced no reduction (p > 0.05) of the DC either in situ or in vitro. No difference was encountered after the softening challenge test (p > 0.05) and no difference was found in µTBS between the two adhesives, both at 24 h (p > 0.05) and after 6 months of storage in distilled water (p > 0.05). However, ATAB:HNT reduced Streptococcus mutans viability (p < 0.05) without a cytotoxic effect on pulp cells (p > 0.05).

Conclusions: GATAB:HNT adhesive demonstrated appropriate polymerization without significant differences in softening after solvent immersion, while concomitantly maintaining reliable bond strength after 6 months of water aging. Moreover, the ATAB:HNT filler can provide antibacterial activity to the adhesive resin without affecting pulp cell viability.

Keywords: dentin bonding agents, anti-bacterial agents, cytotoxicity, drug delivery system