Wir verwenden Cookies, um für diese Website Funktionen wie z.B. Login, einen Warenkorb oder die Sprachwahl zu ermöglichen. Weiterhin nutzen wir für anonymisierte, statistische Auswertungen der Nutzung Google Analytics, welches Cookies setzt. Mehr Informationen finden Sie in unserer Datenschutzerklärung.
OK, ich bin einverstanden Ich möchte keine Google Analytics-Cookies
The Journal of Adhesive Dentistry
Login:
Benutzername:

Kennwort:

Plattform:

Kennwort vergessen?

Registrieren

J Adhes Dent 14 (2012), Nr. 5     15. Okt. 2012
J Adhes Dent 14 (2012), Nr. 5  (15.10.2012)

Seite 447-452, doi:10.3290/j.jad.a23316, PubMed:22518383, Sprache: Englisch


Shear Bond Strength of Self-etching Adhesive Systems with Different pH Values to Bleached and/or CPP-ACP-treated Enamel
Oskoee, Siavash Savadi / Bahari, Mahmoud / Kimyai, Soodabeh / Navimipour, Elmira Jafari / Firouzmandi, Maryam
Purpose: To compare shear bond strengths of three different self-etching adhesive systems of different pH values to enamel bleached with carbamide peroxide, treated with casein phosphopeptide-amorphous calcium phosphate (CPP-ACP), or treated with CPP-ACP subsequent to bleaching with carbamide peroxide.
Materials and Methods: Thirty-six human third molars were cut into 4 sections and randomly assigned to 4 groups (n = 36): group I: no treatment; group II: bleaching; group III: CPP-ACP; group IV: bleaching and CPP-ACP. After surface treatments, the samples of each group were further divided into three subgroups (n = 12) based on the adhesive used. The adhesives Clearfil SE Bond (CSE), AdhesE (ADE), and Adper SE Plus (ADP) were applied, and resin composite cylinders with a diameter of 2 mm and a height of 4 mm were bonded to the enamel. Then the specimens were subjected to shear bond strength testing. Two-way ANOVA and a post-hoc Tukey's test were used for statistical analysis (α = 0.05).
Results: There were significant differences between the adhesive systems (p < 0.001) and surface treatments (p < 0.001), but no significant interactions were observed between these variables (p = 0.78). The CSE adhesive system showed the highest bond strength, and the bleaching procedure reduced bond strengths (p = 0.001). Furthermore, there were no significant differences in shear bond strength values between the control and CPP groups. However, the differences between other groups were statistically significant (p < 0.05).
Conclusion: Bleaching reduced shear bond strength to enamel, but CPP-ACP application did not affect the bond strength to intact and previously bleached enamel. The bond strength of adhesives with different pH values to enamel was material dependant.

Schlagwörter: pH, self-etching adhesives, bleaching, casein phosphopeptide-amorphous calcium phosphate, bond strength